Similar observations were made through the DMA thermograms for the 3:1, 1:1, and 1:3 blends, where a clear trend in decreasing E ′ max of 4887, 3135, and 2941 MPa, respectively, is observed with decreasing loading of the more crystalline PHBU-5 ( Figure 4 C and Table S7 ).
← all excerpts
Tunable and Degradable Dynamic Thermosets from Compatibilized Polyhydroxyalkanoate Blends.